Optical and structural characterization of CdSe:Eu films at different volumes of europium concentration

PDF HTML
  • Diemiruaye Mimi Jeroh*1,
  • Azubike Josiah Ekpunobi1,
  • Donald Nnanyere Okoli1,
  1. Department of Physics and Industrial Physics, Nnamdi Azikiwe University, Awka, Nigeria

Received: 2022-03-16

Accepted: 2022-07-28

Published in Issue 2024-03-08

How to Cite

1.
Jeroh DM, Ekpunobi AJ, Okoli DN. Optical and structural characterization of CdSe:Eu films at different volumes of europium concentration. J Theor Appl phys. 2024 Mar. 8;16(2). Available from: https://oiccpress.com/jtap/article/view/1921
Crossref
Scopus
Google Scholar
Europe PMC

PDF views: 195

HTML views: 14

Abstract

Cadmium selenide films were prepared at different volumes of dopant (Europium) concentration by electrostaticspray-pyrolysis technique. Optical results reveal low absorption and reflection with a corresponding high transmission in the visible region. Strong blue-shift is observed for the band gap energy in all cases of growth, indicating quantum confinement effect. Scanning electron studies reveal relatively smooth surface with smallsized grains on the surface. XRD confirms the crystalline nature of the films having hexagonal (wurtzite) structure with reduction in crystallinity of the film at increased volume of dopant concentration. EDX analysis confirmed the growth of CdSe:Eu film.

Keywords

  • Electrostatic,
  • Hexagonal,
  • Nanomaterials,
  • Spray Pyrolysis,
  • Wurtzite