AbstractIn this work the corrosion resistance of stainless steel 304L coated with Mn-based thin film and post annealed with flow of nitrogen at 723 K in 0.6 M NaCl solution is reported. The latter was performed at three different solution temperatures of 293 K, 313 K and 333 K. X-ray diffraction analysis was used to determine the crystallographical structure and […]
AbstractA method for enhancing the resistance against corrosion of stainless steel 304L coated with 190 nm-thick manganese film and annealed with nitrogen flux at constant temperature (723 K) is reported. The variable quantity in this work is the temperature of the corroding solution (293 K and 333 K). X-ray diffraction analysis was employed to investigate the crystallographical changes of […]