AbstractThe ZnS thin films have been deposited by radio frequency magnetron sputtering at room temperature. Post-deposition rapid thermal annealing treatment was done for the films deposited at different powers ranging from 70 to 100 W. One peak is observed for as-deposited and annealed thin films at around 28.48° corresponding to the (111) reflection plane indicating a […]
AbstractCadmium sulfide (CdS) thin films are deposited on the fluorine doped tin oxide coated glass substrate using the radio frequency magnetron sputtering setup. The effects of annealing in air on the structural, morphological, and optical properties of CdS thin film are studied. Optimal annealing temperature is investigated by annealing the CdS thin film at different […]
AbstractTo obtain a suitable ohmic contact with the lowest resistivity, chromium (Cr) thin films were deposited on transparent conductive oxide indium tin oxide (ITO) by RF sputtering method in argon atmosphere and its electrical properties were optimized. The deposition of Cr thin film has been performed for the layers with thickness of 150, 300 and […]