A series of tungestophosphoric acid and vanadium oxide supported on Mesocellulous Silica Foams (MCFs) featuring a well-defined three-dimensional (3D) mesoporosity were studied with regard to their performance in the photocatalytic activity to degrade Oezine Y (OY). This nanosized mesoporous catalyst (PW12@V-MCF) was characterized by FTIR, XRD, BET and TEM. XRD shows that the structure of […]
Sulfonic acid functionalized nanoporous silica (SBA-Pr-SO3H) with a pore size of 6 nm catalyzed three component coupling of aromatic aldehydes, urea and ethyl acetoacetate to afford the corresponding dihydropyrimidinones under solvent free condition. This new protocol for Biginelli reaction has important advantages such as green synthesis, short reaction time, easy isolation and high yields of […]
Red pine leafs were applied for the green method preparation of MgO nano-plates. The MgO nano-plates were used for the one-pot synthesis of dihydropyrano [3,2-c] chromene derivatives. This procedure is very simple and affords excellent yields. MgO nanoplates were synthesized via a simple precipitation method with the using of an extract solution of red pine […]
5-Substituted-1H-tetrazoles were synthesized by the [3 + 2] cycloaddition of sodium azide with various nitriles in the presence of nickel zirconium phosphate (NiZrP) as an effective heterogeneous catalyst in dimethylsulfoxide at 120 °C. This method has the advantages of good to high yields, simple methodology and easy work-up. The catalyst can be recovered by centrifuging […]
TiCl2/nano-γ-Al2O3 as a new heterogeneous Lewis acid catalyst was synthesized and characterized by FE-SEM, XRD, FT-IR, EDS, XRF, BET and TGA. N-substituted pyrroles have been synthesized via Paal–Knorr reaction in the presence of TiCl2/nano-γ-Al2O3 at room temperature under solvent-free conditions.
BiFeO3 (BFO), Bi0.86Sm0.07Eu0.07FeO3 (BSEFO), and Bi0.86Sm0.07Cd0.07FeO3 (BSCFO) nano powders were prepared by the sol-gel combustion method and the catalytic performances were evaluated in the acetylation reaction of benzyl alcohol. The physical chemical properties of the catalysts were characterized by using XRD, FT-IR, scanning electron microscope (SEM), EDX and BET surface. The efficient acetylation of benzyl […]
In this work, CuO nanoparticles (CuO NPs) was prepared by a simple and green method using Rosmarinus officinalis extract containing phenolic constituents as both the chelating and the stabilizing agents. CuO nanoparticles/polyorthoaminophenol composite (CuO NPs/POAP) as electro-active electrodes for electrocatalytic oxidation of methanol with good uniformity are prepared by electropolymerization. Composite of CuO NPs/POAP was […]
Nano hexagonal wurtzite ZnO has been prepared on zeoliteA by the sono-chemical method. The zeoliteA was mixed into Zinc gel, after stirring for two days, the mixture was irradiated 30 min by ultrasonic probe. The filtrated composite gel was calcinated at 500°C for 3h in furnace. The produced composite was characterized using X-ray diffraction, FT-IR […]
Titania, single-doped and lanthanum-silver co-doped titania nanocomposite were coated on cellulosic and polyacrylonitrile fibers via sol–gel method. The prepared samples were evaluated using x-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive x-ray spectroscopy (EDX), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), photoluminescence spectroscopy (PL) and BET surface area measurement. The photo self-cleaning activity […]
ZnO nanoparticles have been prepared by a simple method in a short period of time. In this synthetic method, the sample was obtained using Zn(CH3COO)2·2H2O and a new template of hexamine salt. Their crystalline structure and morphology were studied by XRD and SEM. The optical properties of the sample were studied by UV–visible spectroscopy. The […]