Using hydrothermal synthesis process a series of Mobil Five (MFI) zeolites were synthesized with silica to alumina ratio (SAR) of 50, 100 and 200. The synthesized MFI zeolites were used to exchange with 0.5%, 1.0% and 2.0% Ca(NO3)2 solutions for modification of MFI zeolites to Ca-MFI zeolite. The formation of MFI zeolite phases was identified […]
Synthesis of nickel oxide nanoparticles (NiO NPs) was carried out by Marrubium astranicum leaf extract. The average of particle sizes for NiO NPs was 40 nm. NiO NPs modified carbon paste electrodes in the absence (CPE/NiO NPs) and the presence of sodium dodecyl sulfate (CPE/NiO NPs/SDS) were examined for the electrocatalytic oxidation of methanol in […]
In this work, the SBA-15-supported dithizone-copper(I) [SBA-15-dtz–Cu(I)] complex as a new heterogeneous catalyst is prepared for the first time. The catalyst prepared is characterized by the FT-IR spectroscopy, SEM, and ICP techniques. This reusable heterogeneous catalyst can be used in the click reactions for the green and facile synthesis of 1,4-disubstituted 1,2,3-triazolesvia a one-pot three-component […]
In-situ synthesis of Ti-incorporated MCM-41 nano catalyst was carried out by the hydrothermal method to prepare a mesoporous catalyst for the oxidative desulfurization reaction (ODS). Oxidative reaction of dibenzothiophene (DBT) as a heavy sulfur compound was evaluated in a solution of n-decane as a model of liquid fuel. The synthesized catalysts were characterized by XRD, […]
Nano-cellulose with high amount of free OH groups could be used as supporting agents for boron trifluoride (BF3). Nano-BF3/cellulose is a solid acid and a biodegradable catalyst which was prepared via reaction of nano-cellulose and BF3. The structure of this catalyst was studied by FT-IR, FESEM, TEM, XRD, EDS, TGA, XRF and BET. In this […]
The preparation, characterization, and immobilization of cobalt (III) salen complex on CoFe2O4@SiO2 nanoparticle (CoFe2O4@SiO2@ Co(III) salen complex) are described. Co(III) salen complex loaded on ferrite cobalt-silica nanoparticle is characterized by TEM, SEM-EDX, VSM and FT-IR analyses. The efficiency of CoFe2O4@SiO2@Co(III) salen complex as a catalyst was carried out in the 3-indolylation reaction of indole with […]
Water samples of 0, 50, and 100 nephelometric turbidity units (NTU) spiked with fecal coliforms (107 CFU/ml) were exposed to natural sunshine in 1l quartz glass tubes fitted with rectors’ compound parabolic concentrators CPCS at two forms CPC1 (whit nanoparticle zinc oxide) and CPC2(without nanoparticle zinc oxide). The samples were characterized using the X-ray powder […]
A proper, atom-economical, straightforward one-pot multicomponent synthetic route for the synthesis of benzopyranophenazines has been presented by the reaction of hydroxynaphthoquinone, o-phenylenediamine, benzaldehydes, and malononitrile with crosslinked sulfonated polyacrylamide (Cross-PAA-SO3H) attached to nano-Fe3O4as an efficient heterogeneous solid acid catalyst under ultrasonic irradiations in ethanol. Experimental simplicity, wide range of products, excellent yields in short reaction […]
The performance of LaMnxNi1-xO3±δ perovskite mixed oxides (x = 0, 0.1, 0.3, 0.5, 0.7, 0.9, 1) which were prepared by different methods, the Pechini and sol-gel methods in the oxidation of greenhouse gases, CH4 and CO, has been investigated. All samples were characterized using Fourier transform infrared spectroscopy, X-ray diffraction, scanning electron microscopy and N2 […]
Mohammad Javad Poursharifi was born in 1971 in Ray City, Iran. He obtained his B.Sc. (1994) from Kharazmi University, Tehran. He then completed his M.Sc. studies in Organic Chemistry (2008) from Islamic Azad University, Saveh Branch, Iran. Currently, he is working towards his Ph.D. under the supervision of Professor Mohammad Majid Mojtahedi and Professor Mahmood […]