Cobalt vanadate (Co3V2O8) nanoparticles were prepared by a hydrothermal process using ammonia metavanadate and cobalt nitrate as precursors and calcined at 450 °C to obtain pure Co3V2O8 nanoparticles. The sample was characterized by scanning electron microscopy, X-ray diffraction, Fourier transform infrared, and UV-visible diffuse reflectance spectroscopy. The characterization analysis confirmed variations in the structure, shape, […]
In this study phase- pure new spinel structure, Mn0.5Cu0.5Cr2O4 was prepared by hydrothermal method successfully and the degradation of Malachite green as an organic pollutant was investigated and compared with CuCr2O4. Purification of obtained nanoparticles was measured by using X-ray diffraction method (XRD) in which crystal structure and the structural properties were studied by using […]
Spinel MgAl2O4 nanopowders were synthesized by one-step solid state reactions using Al(NO3)3.9H2O and MgSO4 raw materials at stoichiometric 1 : 2, Mg : Al molar ratio at a constant reaction temperature of 1000 ºC for 8 h (S1), 10 h (S2) and 24 h (S3). The synthesized materials were characterized by powder X-ray diffraction (PXRD) […]
Nanostructured Ni1-xLnxSb2O6 (Ln = Eu, Gd, Ho and Yb) powders were synthesized via stoichiometric 1:2 Ni:Sb molar ratio by solid state reaction at 800 ºC for 8 h using Ni(NO3)2, Sb2O3, Eu2O3, Gd2O3 and Ho2O3 raw materials. The synthesized materials were characterized by X-ray diffraction (XRD) technique. Structural analyses were done by FullProf program employing […]
The present work reports the Hirshfeld surface analysis and photocatalytic performance of NiFe2O4 nanomaterial. Hirshfeld surface analysis was performed to understand the interaction properties of the NiFe2O4 compound. The active sites including π-π interactions are studied by the analysis. The Hirshfeld data showed that the two wings in the O…O and O…Ni diagrams are created […]