The nano sized TiO2 and ZnO are the most active photocatalysts. Methylene blue was used as a reference molecule for the photocatalytic degradation. The TiO2 and ZnO can totally remove methylene blue dye. The effect of various process parameters like initial concentration, contact time, dose of catalyst and pH on the extent of removal of […]
Porous Silicon (PS) layers have been prepared from p-type silicon wafers of (100) orientation. SEM, XRD, FTIR and PL studies were done to characterize the surface morphological and optical properties of PS. The porosity of the PS samples was determined using the parameters obtained from SEM images by geometric method. The refractive index values of […]
ZnO thin films with preferred orientation along the (002) plane were prepared onto the glass substrates by the sol-gel spin coating method for different post- annealing temperatures. The XRD study confirms that the thin films grown by this method have good crystalline hexagonal wurtzite structure. The optical band gap of the samples was determined from […]
B1-xLaxFeO3 (x = 0.0, 0.025) crystallites were prepared by chemical solution route. XRD analysis confirmed the phase formation of the materials. Thermal characterization was done by DSC-TGA to confirm crystallization and thermal behavior for phase development. Morphological studies by FESEM showed the agglomerated nature of the ferrite and EDX analysis confirmed the degree of doping. […]
Nanotechnology provides the ability to engineer the properties of materials by controlling their size, and this has driven research toward a multitude of potential uses for nanomaterials. This study aimed at biosynthesis and characterization of silver nanoparticles (SNPs) using exopolysaccharides (EPS) of lactic acid bacteria (LAB) and the antimicrobial potential of the biosynthesized SNPs against […]
Bactericidal effect of copper oxide is still a growing area of research even though a lot of experiments have been carried out by the researchers. The present work was designed to explore structural and optical properties of micro-size copper oxide particles (µCuO) synthesized using microwave irradiation. Synthesized samples were characterized with ultraviolet-visible spectroscopy, Fourier transform […]