10.1007/s40097-014-0089-y

The effect of solvents and the thickness on structural, optical and electrical properties of ITO thin films prepared by a sol–gel spin-coating process

HTML PDF
  • Mohsen Moradi-Haji Jafan*1,
  • Mohammad-Reza Zamani-Meymian1,
  • Rahmatollah Rahimi2,
  • Mahboubeh Rabbani2,
  1. Department of Physics (Solid State), Iran University of Science and Technology, Tehran, 16846-13114, IR
  2. Department of Chemistry, Iran University of Science and Technology, Tehran, IR
Cover Image

Published in Issue 28-02-2014

How to Cite

Moradi-Haji Jafan, M., Zamani-Meymian, M.-R., Rahimi, R., & Rabbani, M. (2014). The effect of solvents and the thickness on structural, optical and electrical properties of ITO thin films prepared by a sol–gel spin-coating process. Journal of Nanostructure in Chemistry, 4(1 (March 2014). https://doi.org/10.1007/s40097-014-0089-y
Crossref
Scopus
Google Scholar
Europe PMC

HTML views: 67

PDF views: 81

Abstract

Abstract In this study, tin-doped indium oxide (ITO) thin films were produced by the sol–gel spin-coating technique with an inexpensive salt of indium (In(NO 3 ) 3 ·H 2 O) and SnCl 4 as indium and tin precursors (the molar ratio of In:Sn was 9:1), respectively. Then the prepared thin films were annealed in the temperature of 550 °C under argon atmosphere (the pressure of 10 torr). Polyvinylalcohol (PVA) was used as stabilizers in the synthesis of ITO sol. The prepared ITO thin films were characterized by EDX, XRD, FT-IR, UV–Vis spectroscopy and SEM images. The XRD patterns of the thin films indicated the main peak of the (2 2 2) plane corresponded to indium oxide with high degree of crystallinity. The FT-IR spectroscopy confirmed that indium tin oxide has been prepared by appearance of a peak at 470 cm −1 that can be assigned to the vibrations of In–O bonds. The optical direct band gap of ITO thin films was calculated about 3.98–4.17 eV by optical transmittance measurements. The grain size of ITO nanoparticles was obtained at about 25–50 nm by SEM images. The electrical characterization was done by the four-point probe method to determine the sheet resistance and resistivity. The effects of coating number on ITO thin films properties were investigated. The low resistivity (sheet resistance of 2.5 kΩ/cm 2 ) and highly transparent films were obtained that can be applied as covers on heater windows. Appearance of a peak at 470 cm −1 can be assigned to the vibrations of In–O bonds and are characteristic of cubic In 2 O 3 .

Keywords

  • TCO,
  • Tin-doped indium oxide,
  • ITO,
  • PVA,
  • Sol–gel,
  • Resistance,
  • Transmittance
HTML PDF

References

  1. Zhang et al. (2010) Synthesis of indium tin oxide nanotubes using 2-methoxyethanol as solvent via simple template method (pp. 171-176) https://doi.org/10.1016/j.jallcom.2010.05.079
  2. Moholkar et al. (2008) Effect of precursor concentration on the properties of ITO thin films (pp. 387-392) https://doi.org/10.1016/j.jallcom.2007.09.138
  3. Kerkache et al. (2009) Effect of oxygen partial pressure on the structural and optical properties of dc sputtered ITO thin films (pp. 46-50) https://doi.org/10.1016/j.jallcom.2009.06.103
  4. Mohammadi et al. (2013) Opto-electronic properties of molybdenum doped indium tin oxide nanostructured thin films prepared via sol–gel spin coating (pp. 6953-6961) https://doi.org/10.1016/j.ceramint.2013.02.032
  5. Beaurain et al. (2008) Effects of annealing temperature and heat-treatment duration on electrical properties of sol–gel derived indium-tin-oxide thin films (pp. 4102-4106) https://doi.org/10.1016/j.tsf.2007.10.021
  6. Cho and Yun (2011) Characterization of indium tin oxide (ITO) thin films prepared by a sol–gel spin coating process (pp. 615-619) https://doi.org/10.1016/j.ceramint.2010.09.033
  7. Alam and Cameron (2000) Optical and electrical properties of transparent conductive ITO thin films deposited by sol–gel process (pp. 455-459) https://doi.org/10.1016/S0040-6090(00)01369-9
  8. Jin et al. (2013) Effect of rapid thermal annealing on the properties of spin-coated In–Zn–Sn–O films 13(Suppl 2) (pp. S177-S181) https://doi.org/10.1016/j.cap.2012.12.015
  9. Kwok et al. (1998) Pulsed laser deposited crystalline ultrathin indium tin oxide films and their conduction mechanisms (pp. 299-302) https://doi.org/10.1016/S0040-6090(98)00959-6
  10. Ryabova et al. (1982) Transparent conductive films of In2O3:Sn prepared by the pyrolysis method (pp. 327-332) https://doi.org/10.1016/0040-6090(82)90156-0
  11. Korobov et al. (1994) Structure and conductance evolution of very thin indium oxide films (pp. 2290-2292) https://doi.org/10.1063/1.112721
  12. Ma et al. (1997) Preparation and properties of indium tin oxide films deposited on polyester substrates by reactive evaporation (pp. 200-202) https://doi.org/10.1016/S0040-6090(97)00203-4
  13. Valencia et al. (2008) Structural, electrical and optical analysis of ITO thin films prepared by sol–gel (pp. 1356-1357) https://doi.org/10.1016/j.mejo.2008.01.036
  14. Jiao et al. (2003) The gas sensing characteristics of ITO thin film prepared by sol–gel method (pp. 216-221) https://doi.org/10.1016/S0925-4005(03)00343-5
  15. Kundu and Biswas (2005) Synthesis and photoluminescence property of nanostructured sol–gel indium tin oxide film on glass (pp. 107-110) https://doi.org/10.1016/j.cplett.2005.08.062
  16. Harrison et al. (1994) The effect of preparative conditions on the morphology of indium oxide and hydroxide (pp. 295-299) https://doi.org/10.1007/BF00486259
  17. Biswas et al. (2006) Work function of sol–gel indium tin oxide (ITO) films on glass (pp. 1953-1959) https://doi.org/10.1016/j.apsusc.2006.03.042
  18. Sarhaddi et al. (2010) Effect of post-annealing temperature on nano-structure and energy band gap of indium tin oxide (ITO) nano-particles synthesized by polymerizing complexing sol–gel method (pp. 452-457) https://doi.org/10.1016/j.physe.2010.08.028
  19. Djaoued et al. (1997) sol–gel-prepared ITO films for electrochromic systems (pp. 108-112) https://doi.org/10.1016/S0040-6090(96)09060-8
  20. Legnani et al. (2007) Indium tin oxide films prepared via wet chemical route (pp. 193-197) https://doi.org/10.1016/j.tsf.2007.06.137
  21. Aegerter and Al-Dahoudi (2003) Wet-chemical processing of transparent and antiglare conducting ITO coating on plastic substrates (pp. 81-89) https://doi.org/10.1023/A:1022636112130
  22. Han et al. (2007) Synthesis of indium tin oxide (ITO) and fluorine-doped tin oxide (FTO) nano-powder by sol–gel combustion hybrid method (pp. 1701-1703) https://doi.org/10.1016/j.matlet.2006.07.114
  23. Al-Dahoudi and Aegerter (2006) Comparative study of transparent conductive In2O3:Sn (ITO) coatings made using a sol and a nanoparticle suspension (pp. 193-197) https://doi.org/10.1016/j.tsf.2005.07.273
  24. Ting et al. (2011) Structural and opto-electrical properties of the tin-doped indium oxide thin films fabricated by the wet chemical method with different indium starting materials (pp. 4286-4292) https://doi.org/10.1016/j.tsf.2011.02.004
  25. Benoy et al. (2009) Thickness dependence of the properties of indium tin oxide (ITO) FILMS prepared by activated reactive evaporation (pp. 629-632) https://doi.org/10.1590/S0103-97332009000600003
  26. Huang et al. (2004) The effect of solvent on the etching of ITO electrode (pp. 146-150) https://doi.org/10.1016/j.matchemphys.2003.11.021
  27. Artaki et al. (1986) Solvent effects on the condensation stage of the sol–gel process (pp. 381-395) https://doi.org/10.1016/0022-3093(86)90504-1
  28. Fallah et al. (2007) Influence of heat treatment on structural, electrical, impedance and optical properties of nanocrystalline ITO films grown on glass at room temperature prepared by electron beam evaporation (pp. 69-74) https://doi.org/10.1016/j.physe.2007.01.003
  29. Li et al. (2008) Effects of heat treatment on morphological, optical and electrical properties of ITO films by sol–gel technique (pp. 366-371) https://doi.org/10.1016/S1003-6326(08)60064-3