OICC Press Journal of Theoretical and Applied Physics 2251-7235 10 3 2023 11 17 Size control of L12-FePt3 nanocrystals by spin-coating method 10.1007/s40094-016-0223-y EN OICC Press Authors Various OICC Press Authors Journal Article 2023 11 17 AbstractAnnealing is one of the stages of FePt nanoparticles preparation, during which the transition to a compositionally ordered phase occurs. In order to size and shape control of the nanoparticles in the mentioned stage, it is needed that they be distributed on a suitable surface. In the present work, the spin-coating method is suggested for preparing monolayer from L12-FePt3 nanoparticles colloidal solution on SiO2/Si substrates. FePt3 nanoparticles were gradually deposited as droplets on the center of a 500 rpm rotating substrate. This step was performed in hexane vapor atmosphere without any stopping time. The analyses revealed that a uniform surface distribution was formed so that, after annealing at 600 °C for 1 h the 6.1 nm L12-FePt3 nanoparticles were spherical in shape with standard deviation of 1.5 nm.