@article{Size control of L12-FePt3 nanocrystals by spin-coating method_2023, volume={10}, url={https://oiccpress.com/journal-of-theoretical-and-applied-physics/article/size-control-of-l12-fept3-nanocrystals-by-spin-coating-method-2/}, DOI={10.1007/s40094-016-0223-y}, abstractNote={AbstractAnnealing is one of the stages of FePt nanoparticles preparation, during which the transition to a compositionally ordered phase occurs. In order to size and shape control of the nanoparticles in the mentioned stage, it is needed that they be distributed on a suitable surface. In the present work, the spin-coating method is suggested for preparing monolayer from L12-FePt3 nanoparticles colloidal solution on SiO2/Si substrates. FePt3 nanoparticles were gradually deposited as droplets on the center of a 500 rpm rotating substrate. This step was performed in hexane vapor atmosphere without any stopping time. The analyses revealed that a uniform surface distribution was formed so that, after annealing at 600 °C for 1 h the 6.1 nm L12-FePt3 nanoparticles were spherical in shape with standard deviation of 1.5 nm.}, number={3}, journal={Journal of Theoretical and Applied Physics}, publisher={OICC Press}, year={2023}, month={Nov.}, keywords={FePt nanoparticle, Monolayer, Polyol method, Spin coating} }